Synthesis and electrical properties of lead-free piezoelectric Bi0.5Na0.5TiO3 thin films prepared by Sol-Gel method

Sara Abou Dargham, Freddy Ponchel, Nadine Abboud, M Soueidan, A Ferri, R Desfeux, J Assaad, Denis Remiens, D Zaouk

Onderzoeksoutput: ArticleAcademicpeer review

18 Downloads (Pure)

Samenvatting

Lead-free Bi0.5Na0.5TiO3 (BNT) piezoelectric thin films were deposited on Pt/TiOx/SiO2/Si substrates by Sol-Gel method. A dense and well crystallized thin film with a perovskite phase was obtained by annealing the film at 700ºC in a rapid thermal processing system. The relative dielectric constant and loss tangent at 12 kHz, of BNT thin film with 350 nm thickness, were 425 and 0.07, respectively. Ferroelectric hysteresis measurements indicated a remnant polarization value of 9 µC/cm2and a coercive field of 90 kV/cm. Piezoelectric measurements at the macroscopic level were also performed: a piezoelectric coefficient (d33effmax) of 47 pm/V at E = 190 kV/cm was obtained. The piezoresponse force microscopy data confirmed that BNT thin films present ferroelectric and piezoelectric behavior at the nanoscale level.
Originele taal-2English
Pagina's (van-tot)1450 - 1455
TijdschriftJournal of the European Ceramic Society
Volume38
Nummer van het tijdschrift4
StatusPublished - apr. 2018
Extern gepubliceerdJa

Keywords

  • piëzo-elektrisch
  • loodvrij
  • dunne films
  • BNT

Vingerafdruk

Duik in de onderzoeksthema's van 'Synthesis and electrical properties of lead-free piezoelectric Bi0.5Na0.5TiO3 thin films prepared by Sol-Gel method'. Samen vormen ze een unieke vingerafdruk.

Citeer dit