Shear bond strength of two composite resin cements to multiphase composite resin after different surface treatments and two glass-ceramics

Maurits C.F.M. de Kuijper, Marco M.M. Gresnigt, Wouter Kerdijk, Marco S. Cune

    Research output: Contribution to journalArticleAcademicpeer-review

    Abstract

    AIM: To compare the shear bond strength (SBS) after aging of two dual-curing composite resin cements to multiphase composite resin (experiment) and glass-ceramics (control).

    METHODS: Seventy computer-aided design/computer-aided manufacturing (CAD/CAM) blocks were prepared: 24 multiphase composite resin blocks (Lava Ultimate; experiment), and 12 control blocks (groups 5 and 6: 6 IPS e.max CAD, 6 IPS Empress CAD). Surface treatments of the experiment groups were: 1) Al2O3 airborne particle abrasion; 2) bur-roughening; 3) silica-coated aluminum oxide particle abrasion; and 4) hydrofluoric (HF) acid etching. Per study group, Variolink II (a) and RelyX Ultimate (b) were used as cements. Per treatment group, four cement cylinders were adhered to the conditioned blocks (n = 12). After thermocyclic aging (10.000x, 5°C to 55°C), notch-edge shear testing was applied. Modes of failure were examined. A P value of 0.05 was considered significant.

    RESULTS: Groups 1a (18.68 ± 3.81) and 3a (17.09 ± 3.40) performed equally to 6a (20.61 ± 4.10). Group 5a (14.39 ± 2.80) did not significantly differ from groups 1a, 3a, and 4a (15.21 ± 4.29). Group 2a (11.61 ± 3.39) showed the lowest bond strength. For the RelyX Ultimate specimens, mean bond strengths were: 1b (18.12 ± 2.84) > 4b (15.57 ± 2.31) > 2b (12.34 ± 1.72) = 3b (11.54 ± 2.45) = 6b (12.31 ± 1.87) > 5b (0.78 ± 0.89). Failure mode analysis showed a significant association between bond strength values and modes of failure (chi-square).

    CONCLUSION: The SBS of the composite cements to the multiphase composite resin that was treated by Al2O3 or silica-coated aluminum oxide particle abrasion is comparable to the bond of the control groups.

    Original languageEnglish
    Pages (from-to)40-50
    JournalThe international journal of esthetic dentistry
    Volume14
    Issue number1
    Publication statusPublished - 5 Feb 2019

    Keywords

    • dentistry

    Cite this

    @article{a9212c61d39d4436967a15d1fea524eb,
    title = "Shear bond strength of two composite resin cements to multiphase composite resin after different surface treatments and two glass-ceramics",
    abstract = "AIM: To compare the shear bond strength (SBS) after aging of two dual-curing composite resin cements to multiphase composite resin (experiment) and glass-ceramics (control).METHODS: Seventy computer-aided design/computer-aided manufacturing (CAD/CAM) blocks were prepared: 24 multiphase composite resin blocks (Lava Ultimate; experiment), and 12 control blocks (groups 5 and 6: 6 IPS e.max CAD, 6 IPS Empress CAD). Surface treatments of the experiment groups were: 1) Al2O3 airborne particle abrasion; 2) bur-roughening; 3) silica-coated aluminum oxide particle abrasion; and 4) hydrofluoric (HF) acid etching. Per study group, Variolink II (a) and RelyX Ultimate (b) were used as cements. Per treatment group, four cement cylinders were adhered to the conditioned blocks (n = 12). After thermocyclic aging (10.000x, 5°C to 55°C), notch-edge shear testing was applied. Modes of failure were examined. A P value of 0.05 was considered significant.RESULTS: Groups 1a (18.68 ± 3.81) and 3a (17.09 ± 3.40) performed equally to 6a (20.61 ± 4.10). Group 5a (14.39 ± 2.80) did not significantly differ from groups 1a, 3a, and 4a (15.21 ± 4.29). Group 2a (11.61 ± 3.39) showed the lowest bond strength. For the RelyX Ultimate specimens, mean bond strengths were: 1b (18.12 ± 2.84) > 4b (15.57 ± 2.31) > 2b (12.34 ± 1.72) = 3b (11.54 ± 2.45) = 6b (12.31 ± 1.87) > 5b (0.78 ± 0.89). Failure mode analysis showed a significant association between bond strength values and modes of failure (chi-square).CONCLUSION: The SBS of the composite cements to the multiphase composite resin that was treated by Al2O3 or silica-coated aluminum oxide particle abrasion is comparable to the bond of the control groups.",
    keywords = "dentistry, tandheelkunde",
    author = "{de Kuijper}, {Maurits C.F.M.} and Gresnigt, {Marco M.M.} and Wouter Kerdijk and Cune, {Marco S.}",
    year = "2019",
    month = "2",
    day = "5",
    language = "English",
    volume = "14",
    pages = "40--50",
    journal = "The international journal of esthetic dentistry",
    issn = "2198-591X",
    publisher = "Quintessence Publishing Co.",
    number = "1",

    }

    Shear bond strength of two composite resin cements to multiphase composite resin after different surface treatments and two glass-ceramics. / de Kuijper, Maurits C.F.M.; Gresnigt, Marco M.M.; Kerdijk, Wouter; Cune, Marco S.

    In: The international journal of esthetic dentistry, Vol. 14, No. 1, 05.02.2019, p. 40-50.

    Research output: Contribution to journalArticleAcademicpeer-review

    TY - JOUR

    T1 - Shear bond strength of two composite resin cements to multiphase composite resin after different surface treatments and two glass-ceramics

    AU - de Kuijper, Maurits C.F.M.

    AU - Gresnigt, Marco M.M.

    AU - Kerdijk, Wouter

    AU - Cune, Marco S.

    PY - 2019/2/5

    Y1 - 2019/2/5

    N2 - AIM: To compare the shear bond strength (SBS) after aging of two dual-curing composite resin cements to multiphase composite resin (experiment) and glass-ceramics (control).METHODS: Seventy computer-aided design/computer-aided manufacturing (CAD/CAM) blocks were prepared: 24 multiphase composite resin blocks (Lava Ultimate; experiment), and 12 control blocks (groups 5 and 6: 6 IPS e.max CAD, 6 IPS Empress CAD). Surface treatments of the experiment groups were: 1) Al2O3 airborne particle abrasion; 2) bur-roughening; 3) silica-coated aluminum oxide particle abrasion; and 4) hydrofluoric (HF) acid etching. Per study group, Variolink II (a) and RelyX Ultimate (b) were used as cements. Per treatment group, four cement cylinders were adhered to the conditioned blocks (n = 12). After thermocyclic aging (10.000x, 5°C to 55°C), notch-edge shear testing was applied. Modes of failure were examined. A P value of 0.05 was considered significant.RESULTS: Groups 1a (18.68 ± 3.81) and 3a (17.09 ± 3.40) performed equally to 6a (20.61 ± 4.10). Group 5a (14.39 ± 2.80) did not significantly differ from groups 1a, 3a, and 4a (15.21 ± 4.29). Group 2a (11.61 ± 3.39) showed the lowest bond strength. For the RelyX Ultimate specimens, mean bond strengths were: 1b (18.12 ± 2.84) > 4b (15.57 ± 2.31) > 2b (12.34 ± 1.72) = 3b (11.54 ± 2.45) = 6b (12.31 ± 1.87) > 5b (0.78 ± 0.89). Failure mode analysis showed a significant association between bond strength values and modes of failure (chi-square).CONCLUSION: The SBS of the composite cements to the multiphase composite resin that was treated by Al2O3 or silica-coated aluminum oxide particle abrasion is comparable to the bond of the control groups.

    AB - AIM: To compare the shear bond strength (SBS) after aging of two dual-curing composite resin cements to multiphase composite resin (experiment) and glass-ceramics (control).METHODS: Seventy computer-aided design/computer-aided manufacturing (CAD/CAM) blocks were prepared: 24 multiphase composite resin blocks (Lava Ultimate; experiment), and 12 control blocks (groups 5 and 6: 6 IPS e.max CAD, 6 IPS Empress CAD). Surface treatments of the experiment groups were: 1) Al2O3 airborne particle abrasion; 2) bur-roughening; 3) silica-coated aluminum oxide particle abrasion; and 4) hydrofluoric (HF) acid etching. Per study group, Variolink II (a) and RelyX Ultimate (b) were used as cements. Per treatment group, four cement cylinders were adhered to the conditioned blocks (n = 12). After thermocyclic aging (10.000x, 5°C to 55°C), notch-edge shear testing was applied. Modes of failure were examined. A P value of 0.05 was considered significant.RESULTS: Groups 1a (18.68 ± 3.81) and 3a (17.09 ± 3.40) performed equally to 6a (20.61 ± 4.10). Group 5a (14.39 ± 2.80) did not significantly differ from groups 1a, 3a, and 4a (15.21 ± 4.29). Group 2a (11.61 ± 3.39) showed the lowest bond strength. For the RelyX Ultimate specimens, mean bond strengths were: 1b (18.12 ± 2.84) > 4b (15.57 ± 2.31) > 2b (12.34 ± 1.72) = 3b (11.54 ± 2.45) = 6b (12.31 ± 1.87) > 5b (0.78 ± 0.89). Failure mode analysis showed a significant association between bond strength values and modes of failure (chi-square).CONCLUSION: The SBS of the composite cements to the multiphase composite resin that was treated by Al2O3 or silica-coated aluminum oxide particle abrasion is comparable to the bond of the control groups.

    KW - dentistry

    KW - tandheelkunde

    M3 - Article

    VL - 14

    SP - 40

    EP - 50

    JO - The international journal of esthetic dentistry

    JF - The international journal of esthetic dentistry

    SN - 2198-591X

    IS - 1

    ER -